| Grade | C | Mn | Si | P | S | Cr | Nb + Ta | Co | Mo | Fe | Al | Ti | Ni |
| 625 | ≤0.10 | ≤0.50 | ≤0.50 | ≤0.015 | ≤0.015 | 20.0 - 23.0 | 3.15 -4.15 | ≤1.0 | 8.0-10.0 | ≤5.0 | ≤0.40 | ≤0.40 | Bal |
| Material | Form and Condition | Tensile Strength MPa | Yield Strength (0.2% Offset) | Elongation 4D(%) | Hardness HB | ||
| ksi | MPa | ksi | MPa | ||||
| Alloy 625 Bar | Annealed | ≥120 | ≥827 | ≥60 | ≥414 | ≥30 | ≤ 287 HB |
| Alloy 625 Sheet | Annealed | ≥120 | ≥827 | ≥60 | ≥414 | ≥30 | 145-240 |
| Alloy 625 Tube3 | Annealed | ≥120 | ≥827 | ≥60 | ≥414 | ≥30 | - |
| Alloy 625 Tube4 | Solution annealed | ≥100 | ≥690 | ≥40 | ≥276 | ||
Note:
1. Hot forming quality pipe and tubing is furnished to chemical requirements and surface inspection only. No tensile properties are required.
2. The minimum strength values apply only to tubing in straight lengths.
3. Annealed at 1600 F (871 °C) minimum.
4. Solution annealed at 2000 °F (1093 °C) minimum, with or without subsequent stabilization anneal at 1800 °F (982 °C) minimum to increase resistance to sensitization.
Q1:What product information must I provide before making a purchase?
Please provide the Grade, Outside Diameter, Thickness, and surfacetreatment requirements, as well as the quantities you require.
Q2:What shipping ports are there?
We normally ship from Shanghai and Ningbo ports.
Q3:What are your payment terms?
30% T/T in advance and 70% balance before shipment or based on BL copy or LC at sight.
Q4:What about product pricing information?
Prices vary due to changes in raw material prices on a regular basis.
Q5:Is it possible to send samples?
Of course, we offer free samples and express shipping to customers all over the world.
Q6:Do you offer a service for customized products?
Yes, we can produce according to your specifications and drawings.
|
|
| MOQ: | 100KGS |
| Price: | 31.5 USD/KG |
| Standard Packaging: | Export Packing |
| Delivery Period: | 7 Days |
| Payment Method: | L/C, T/T |
| Supply Capacity: | 50000KGS |
| Grade | C | Mn | Si | P | S | Cr | Nb + Ta | Co | Mo | Fe | Al | Ti | Ni |
| 625 | ≤0.10 | ≤0.50 | ≤0.50 | ≤0.015 | ≤0.015 | 20.0 - 23.0 | 3.15 -4.15 | ≤1.0 | 8.0-10.0 | ≤5.0 | ≤0.40 | ≤0.40 | Bal |
| Material | Form and Condition | Tensile Strength MPa | Yield Strength (0.2% Offset) | Elongation 4D(%) | Hardness HB | ||
| ksi | MPa | ksi | MPa | ||||
| Alloy 625 Bar | Annealed | ≥120 | ≥827 | ≥60 | ≥414 | ≥30 | ≤ 287 HB |
| Alloy 625 Sheet | Annealed | ≥120 | ≥827 | ≥60 | ≥414 | ≥30 | 145-240 |
| Alloy 625 Tube3 | Annealed | ≥120 | ≥827 | ≥60 | ≥414 | ≥30 | - |
| Alloy 625 Tube4 | Solution annealed | ≥100 | ≥690 | ≥40 | ≥276 | ||
Note:
1. Hot forming quality pipe and tubing is furnished to chemical requirements and surface inspection only. No tensile properties are required.
2. The minimum strength values apply only to tubing in straight lengths.
3. Annealed at 1600 F (871 °C) minimum.
4. Solution annealed at 2000 °F (1093 °C) minimum, with or without subsequent stabilization anneal at 1800 °F (982 °C) minimum to increase resistance to sensitization.
Q1:What product information must I provide before making a purchase?
Please provide the Grade, Outside Diameter, Thickness, and surfacetreatment requirements, as well as the quantities you require.
Q2:What shipping ports are there?
We normally ship from Shanghai and Ningbo ports.
Q3:What are your payment terms?
30% T/T in advance and 70% balance before shipment or based on BL copy or LC at sight.
Q4:What about product pricing information?
Prices vary due to changes in raw material prices on a regular basis.
Q5:Is it possible to send samples?
Of course, we offer free samples and express shipping to customers all over the world.
Q6:Do you offer a service for customized products?
Yes, we can produce according to your specifications and drawings.