| Product Name | Hastelloy Round Bar |
| Material | Incoloy 800(N08800) Incoloy 800H(N08810) Incoloy 825(N08825) X2NiCrAITi3220 NiCr21Mo Inconel 600(N06600)Inconel 690(N06690) Inconel 625(N06625) LC-NiCr15Fe NiCr23Fe NiCr29Fe NiCr22Mo9Nb Hastelloy B C C-4 Hastelloy C276 NiMo16Cr15W |
| Tolorance | +-5% |
| Out Diameter | 3mm-300mm |
| Length | 1m,3m,6m,12m or as the customer's demand |
| Surface Treatment | Polished,Hair Line,Brush,Mirror Finish |
| Manufacture Method | Hot Rolled,Cold Rolled,Cold Drawn,Extruded |
Application |
Nickel Incoloy Alloy Pipe widely used in Chemical processing Pollution-control Oil and gas well piping Nuclear fuel reprocessing Components in pickling equipment like heating coils, tanks, baskets and chains Acid production |
| Steel Grade | N06455, 2.4610 | Type | Seamless |
| Standard | ASTM, AISI, GB, DIN, JIS | Certification | ISO,SGS,BV,ISO/CE/SGS |
| Length | 15000mm Max, Customized | Thickness | 0.508-50.8mm |
| Technique | Cold Rolled, Cold Drawn | Min./Avg. | Avg. |
| Outer Diameter | 6.35-406.4mm, Customized | Finish | Brush Polish Cold Drawn, Pickled,Bright Annealed |
Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 alloy is a nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. This alloy resists the formation of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as welded condition. C-4 alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900°F (1038°C).
Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 alloy has exceptional resistance to wide variety of chemical process environments. These include hot contaminated mineral acids, solvents, chlorine nd chlorine contaminated media (organic and inorganic), dry chlorine, formic acid and acetic acid, acetic anhydride, and seawater and brine solutions.
Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy can be forged, hot-upset, and impact extruded. Although the alloy tends to work-harden, it can be successfully deep-drawn, spun, press formed or punched. All of the common methods of welding can be used to weld Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy, although the oxy-acetylene and submerged arc processes are not recommended when the fabricated item is intended for use in corrosion service. Special precautions should be taken to avoid excessive heat input.
Hastelloy C4 Alloy ASTM B619 B622 B626 N06645 Alloy Chemical compostion:
ASTM B622 N06645 Hastelloy C4 Alloy Chemical Composition:
| Ni | Mo | Fe | C | Co | Cr | Mn | Si | Ti | W | Al | Cu | V | P | S | Zr | Nb | Ta |
| Rem. | 14.0- 17.0 | 3.0 max | 0.015 max | 2.0 max | 14.0- 18.0 | 1.0 max | 0.08 max |
0.70 max | 1.0 max | 0.04 max | 0.03 max |
DIN 17744 2002 2.4610 NiMo16Cr16Ti Hastelloy C4 Alloy Chemical Composition:
| Ni | Mo | Fe | C | Co | Cr | Mn | Si | Ti | W | Al | Cu | V | P | S | Zr | Nb | Ta |
| Rem. | 14.0- 17.0 | 3.0 max | 0.015 max | 2.0 max | 14.0- 18.0 | 1.0 max | 0.08 max |
0.70 max | 0.50 max | 0.025 max | 0.015 max |
Alloy C-4 is a nickel-chromium-molybdenum alloy with outstanding high temperature stability. This alloy resists the formation of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as-welded condition. Alloy C-4 alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900°F (1038°C).
Components used in wastewater treatment
Components used in chemical processing
Nuclear fuel processing
Nickel: Balance
Chromium:14.00-18.00
Molybdenum: 14.00-17.00
Iron: 3.00 max
Cobalt: 2.00 max
Manganese: 1.00 max
Carbon: 0.015 max
Silicon: 0.08 max
Phosphorus: 0.04 max
Sulfur: 0.03 max
Titanium: 0.70 max
Ultimate Tensile Strength: 100 KSI min (690 MPa min)
Yield Strength: 40 KSI min (276 MPa min)
Elongation: 40% min
Hardness: Rb 100 max (aim)
Alloy C-4can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
|
|
| MOQ: | 10KGS |
| Price: | USD20.45/KG |
| Standard Packaging: | Wooden Box |
| Delivery Period: | 7 Days |
| Payment Method: | L/C, T/T, Western Union |
| Supply Capacity: | 50000KGS |
| Product Name | Hastelloy Round Bar |
| Material | Incoloy 800(N08800) Incoloy 800H(N08810) Incoloy 825(N08825) X2NiCrAITi3220 NiCr21Mo Inconel 600(N06600)Inconel 690(N06690) Inconel 625(N06625) LC-NiCr15Fe NiCr23Fe NiCr29Fe NiCr22Mo9Nb Hastelloy B C C-4 Hastelloy C276 NiMo16Cr15W |
| Tolorance | +-5% |
| Out Diameter | 3mm-300mm |
| Length | 1m,3m,6m,12m or as the customer's demand |
| Surface Treatment | Polished,Hair Line,Brush,Mirror Finish |
| Manufacture Method | Hot Rolled,Cold Rolled,Cold Drawn,Extruded |
Application |
Nickel Incoloy Alloy Pipe widely used in Chemical processing Pollution-control Oil and gas well piping Nuclear fuel reprocessing Components in pickling equipment like heating coils, tanks, baskets and chains Acid production |
| Steel Grade | N06455, 2.4610 | Type | Seamless |
| Standard | ASTM, AISI, GB, DIN, JIS | Certification | ISO,SGS,BV,ISO/CE/SGS |
| Length | 15000mm Max, Customized | Thickness | 0.508-50.8mm |
| Technique | Cold Rolled, Cold Drawn | Min./Avg. | Avg. |
| Outer Diameter | 6.35-406.4mm, Customized | Finish | Brush Polish Cold Drawn, Pickled,Bright Annealed |
Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 alloy is a nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. This alloy resists the formation of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as welded condition. C-4 alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900°F (1038°C).
Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 alloy has exceptional resistance to wide variety of chemical process environments. These include hot contaminated mineral acids, solvents, chlorine nd chlorine contaminated media (organic and inorganic), dry chlorine, formic acid and acetic acid, acetic anhydride, and seawater and brine solutions.
Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy can be forged, hot-upset, and impact extruded. Although the alloy tends to work-harden, it can be successfully deep-drawn, spun, press formed or punched. All of the common methods of welding can be used to weld Hastelloy C4 Alloy ASTM B619 B622 B626 N06455 N06455 alloy, although the oxy-acetylene and submerged arc processes are not recommended when the fabricated item is intended for use in corrosion service. Special precautions should be taken to avoid excessive heat input.
Hastelloy C4 Alloy ASTM B619 B622 B626 N06645 Alloy Chemical compostion:
ASTM B622 N06645 Hastelloy C4 Alloy Chemical Composition:
| Ni | Mo | Fe | C | Co | Cr | Mn | Si | Ti | W | Al | Cu | V | P | S | Zr | Nb | Ta |
| Rem. | 14.0- 17.0 | 3.0 max | 0.015 max | 2.0 max | 14.0- 18.0 | 1.0 max | 0.08 max |
0.70 max | 1.0 max | 0.04 max | 0.03 max |
DIN 17744 2002 2.4610 NiMo16Cr16Ti Hastelloy C4 Alloy Chemical Composition:
| Ni | Mo | Fe | C | Co | Cr | Mn | Si | Ti | W | Al | Cu | V | P | S | Zr | Nb | Ta |
| Rem. | 14.0- 17.0 | 3.0 max | 0.015 max | 2.0 max | 14.0- 18.0 | 1.0 max | 0.08 max |
0.70 max | 0.50 max | 0.025 max | 0.015 max |
Alloy C-4 is a nickel-chromium-molybdenum alloy with outstanding high temperature stability. This alloy resists the formation of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in the as-welded condition. Alloy C-4 alloy also has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900°F (1038°C).
Components used in wastewater treatment
Components used in chemical processing
Nuclear fuel processing
Nickel: Balance
Chromium:14.00-18.00
Molybdenum: 14.00-17.00
Iron: 3.00 max
Cobalt: 2.00 max
Manganese: 1.00 max
Carbon: 0.015 max
Silicon: 0.08 max
Phosphorus: 0.04 max
Sulfur: 0.03 max
Titanium: 0.70 max
Ultimate Tensile Strength: 100 KSI min (690 MPa min)
Yield Strength: 40 KSI min (276 MPa min)
Elongation: 40% min
Hardness: Rb 100 max (aim)
Alloy C-4can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.