EN 10088-2-2005 1.4418 X4CrNiMo16-5-1 Martensitic Stainless Steel Round Bar OD 250mm
| Grade : | X4CrNiMo16-5-1 | ||||||||
| Number: | 1.4418 | ||||||||
| Classification: | Martensitic stainless steel | ||||||||
| Density: | 7.7 g/cm ³ | ||||||||
| Standard: |
|
||||||||
| Equivalent grades: | 1.4418 |
| Tighter carbon ranges may be agreed at the time of enquery and order Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Mo | N |
| max 0.06 | max 0.7 | max 1.5 | 4 - 6 | max 0.04 | max 0.015 | 15 - 17 | 0.8 - 1.5 | max 0.02 |
| Rm - Tensile strength (MPa) (+QT) | 760-1100 |
| Rm - Tensile strength (MPa) (+A) | 1100 |
| Rp0.2 0.2% proof strength (MPa) (+QT) | 550-700 |
| KV - Impact energy (J) (+QT) | +20° 55-90 |
-20° 40 |
| A - Min. elongation at fracture (%) longitud., (+QT) | 16 |
| A - Min. elongation at fracture (%) transverse, (+QT) | 14 |
| Brinell hardness (HB): (+A) | 320 |
| EU EN |
France AFNOR |
Sweden SS |
||
| X4CrNiMo16-5-1 |
|
|
|
|
| MOQ: | 50KG |
| Price: | 3.15 USD/KG |
| Standard Packaging: | Wooden Box |
| Delivery Period: | 7 Days |
| Payment Method: | L/C, Western Union, T/T |
| Supply Capacity: | 80000KGS |
EN 10088-2-2005 1.4418 X4CrNiMo16-5-1 Martensitic Stainless Steel Round Bar OD 250mm
| Grade : | X4CrNiMo16-5-1 | ||||||||
| Number: | 1.4418 | ||||||||
| Classification: | Martensitic stainless steel | ||||||||
| Density: | 7.7 g/cm ³ | ||||||||
| Standard: |
|
||||||||
| Equivalent grades: | 1.4418 |
| Tighter carbon ranges may be agreed at the time of enquery and order Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Mo | N |
| max 0.06 | max 0.7 | max 1.5 | 4 - 6 | max 0.04 | max 0.015 | 15 - 17 | 0.8 - 1.5 | max 0.02 |
| Rm - Tensile strength (MPa) (+QT) | 760-1100 |
| Rm - Tensile strength (MPa) (+A) | 1100 |
| Rp0.2 0.2% proof strength (MPa) (+QT) | 550-700 |
| KV - Impact energy (J) (+QT) | +20° 55-90 |
-20° 40 |
| A - Min. elongation at fracture (%) longitud., (+QT) | 16 |
| A - Min. elongation at fracture (%) transverse, (+QT) | 14 |
| Brinell hardness (HB): (+A) | 320 |
| EU EN |
France AFNOR |
Sweden SS |
||
| X4CrNiMo16-5-1 |
|
|