Stainless steel grade 436L is ferritic steel that has excellent oxidation resistance and corrosion testing compared to grade 409. The addition of molybdenum in this alloy enhances pitting resistance. It is also resistant to stress corrosion cracking in the presence of chlorides, and has excellent formability.
The following sections will discuss in detail about stainless steel grade 436L.
The chemical composition of stainless steel grade 436L is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 80.49 |
| Chromium, Cr | 17.3 |
| Molybdenum, Mo | 1 |
| Nickel, Ni | 0.3 |
| Manganese, Mn | 0.3 |
| Silicon, Si | 0.3 |
| Titanium, Ti | 0.3 |
| Carbon, C | 0.01 |
The mechanical properties of stainless steel grade 436L are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 441-517 MPa | 64000-75000 psi |
| Yield strength | 276-345 MPa | 40000-50000 psi |
| Elongation at break | 28-35% | 28-35% |
| Hardness, Rockwell B | 74-85 | 74-85 |
Stainless steel grade 436L is used in automotive exhaust applications.
|
|
| MOQ: | 100KGS |
| Price: | 2.5 USD/KG |
| Standard Packaging: | Wooden Pallet |
| Delivery Period: | 7 Days |
| Payment Method: | L/C, T/T |
| Supply Capacity: | 50000KGS |
Stainless steel grade 436L is ferritic steel that has excellent oxidation resistance and corrosion testing compared to grade 409. The addition of molybdenum in this alloy enhances pitting resistance. It is also resistant to stress corrosion cracking in the presence of chlorides, and has excellent formability.
The following sections will discuss in detail about stainless steel grade 436L.
The chemical composition of stainless steel grade 436L is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 80.49 |
| Chromium, Cr | 17.3 |
| Molybdenum, Mo | 1 |
| Nickel, Ni | 0.3 |
| Manganese, Mn | 0.3 |
| Silicon, Si | 0.3 |
| Titanium, Ti | 0.3 |
| Carbon, C | 0.01 |
The mechanical properties of stainless steel grade 436L are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 441-517 MPa | 64000-75000 psi |
| Yield strength | 276-345 MPa | 40000-50000 psi |
| Elongation at break | 28-35% | 28-35% |
| Hardness, Rockwell B | 74-85 | 74-85 |
Stainless steel grade 436L is used in automotive exhaust applications.